Derivation of elastic fracture toughness for ductile metal pipes with circumferential external cracks under combined tension and bending
Engineering fracture mechanics, Vol.178, pp.39-49
01/06/2017
Metrics
12 Record Views
UN Sustainable Development Goals (SDGs)
This output has contributed to the advancement of the following goals:
Source: InCites
Abstract
Linear elastic fracture mechanics has been widely employed for fracture analysis of cracked pipes. For ductile metal pipes, the existence of plasticity eases the stress concentration at the crack front, which increases the fracture toughness of the pipe. Therefore, when using linear elastic fracture mechanics to predict the fracture failure of ductile pipes, the plastic portion of the fracture toughness should be excluded. This paper intends to derive an analytical model of elastic fracture toughness for ductile metal pipes with circumferential external surface cracks under combined axial tension and bending. The derived elastic fracture toughness is a function of crack geometry, material properties and loading conditions of the cracked pipe. The significance of the derived model is that the well established linear elastic fracture mechanics can be used for ductile materials in predicting the fracture failure. It is found in the paper that, the elastic fracture toughness increases with the increase of the internal pressure of the pipe and that an increase in fracture toughness and yield strength of the pipe materials will result in a more ductile and brittle pipe failure respectively. The derived analytical model enables more accurate prediction of fracture failure of ductile metal pipes with circumferential external cracks.
Details
- Title
- Derivation of elastic fracture toughness for ductile metal pipes with circumferential external cracks under combined tension and bending
- Creators
- Chun-Qing Li - RMIT UniversityGuoyang Fu - RMIT UniversityWei Yang - Victoria UniversityShangtong Yang - University of Strathclyde
- Publication Details
- Engineering fracture mechanics, Vol.178, pp.39-49
- Publisher
- Elsevier Ltd
- Identifiers
- 991013126110002368
- Copyright
- (c) 2017 Elsevier Ltd. All rights reserved.
- Academic Unit
- Faculty of Science and Engineering
- Language
- English
- Resource Type
- Journal article